Product Data Sheet Show all documents
SikaTop®-122

SikaTop®-122

Fiber reinforced polymer modified repair mortar

SikaTop®-122 is a two-component high performance, cement based, polymer modified, fiber reinforced, structural concrete repair mortar. Suitable for horizontal, vertical and overhead applications.

  • Excellent adherence
  • Good mechanical strength
  • High compression resistances at all ages
  • Good water and oil resistance
  • Increase resistance to salt water, chlorides and carbonation
  • Synthetic fiber reinforced
  • High abrasion, wear and impact resistance
Product Data Sheet Show all documents

Usage

  • Use as concrete repair mortar for repairing damages in concrete structures like beams, piles, slabs, posts, pipes, precast elements, etc.
  • Use in horizontal, vertical and overhead applications without the need of formworks.
  • Repairing concrete defects like pores, honeycombs and level irregularities.
  • Use as high adhesion render, with high abrasion resistance, waterproof to protect, repair and maintain concrete structures.
 

Advantages

  • Excellent adherence
  • Good mechanical strength
  • High compression resistances at all ages
  • Good water and oil resistance
  • Increase resistance to salt water, chlorides and carbonation
  • Synthetic fiber reinforced
  • High abrasion, wear and impact resistance

Packaging

30 kg set: A (4.1 kg) + B (25.9 kg)

Colour

Mixed components light grey.

Component A: white liquid

Component B: grey powder

Product Details

Product Information

Composition

Cement, selected aggregates and additives

Shelf life

9 months from date of production if stored properly in unopened original packing.

Storage conditions

Store properly in undamaged original sealed packaging, in dry cool conditions between +5 °C and +30 °C.

Density

~2.2 kg/L at +20 °C (mixed density A+B)
System information

System Structure

Repair Mortar

SikaTop®-122

Normal Use

Levelling Mortar

SikaTop®-121Normal Use
Technical Information

Compressive Strength

7 days

~40 N/mm2

28 days~52 N/mm2

Tensile Strength in Flexure

7 days

~7 N/mm2

28 days~12 N/mm2

Tensile Adhesion Strength

28 days

~1.5 N/mm2

(concrete failure)

Application

Application Information

Mixing Ratio

Parts by weight: A : B = 1 : 6.3

Layer Thickness

Minimum 5 mm / maximum 20 mm

Ambient Air Temperature

+8 °C minimum; +30 °C maximum

Substrate Temperature

+8 °C minimum; +30 °C maximum

Pot Life

~25 minutes (at +30 °C)
Consumption

Consumption

This depends on the substrate roughness and thickness of the layer applied. As a guide, ~22 kg of powder per cm thick per m2

Yield

30 kg of product yields approximately 13 litres of mortar
Application steps

MIXING

SikaTop®-122 can be mixed with a low speed (<250 rpm) hand drill mixer.

Shake Component A (liquid) and pour it into a suitable mixing vessel. While mixing add Component B (powder) into the mix. Mix the two components together for a minimum 3 minutes. DO NOT ADD WATER.

APPLICATION

SikaTop®-122 can be applied manually using traditional techniques. Thoroughly pre-wet the prepared substrate a recommended 2 hours before application. Keep the surface wet and do not allow to dry. Before application remove excess water e.g. with a clean sponge. The surface shall appear a dark matt appearance without glistening and surface pores and pits shall not contain water.

 

Apply first a scratch coat by firmly scrapping the repair mortar over the substrate surface to form a thin layer and fill any pores or pits in the surface. Ensure the whole surface to be repaired is covered by the scratch coat. Build up layers from bottom to top by pressing mortar well into the repair area.

The surface can be finished according to the requirements using a float while wet or with a relevant rough-cast tool as soon as the mortar has started to stiffen.

CURING TREATMENT

Protect the fresh mortar immediately from premature drying using an appropiate curing method e.g. curing compound, moist geotextile membrane, polythene sheet, etc.

CLEANING OF EQUIPMENT

Clean all tools and application equipment with water immediately after use. Hardened material can only be mechanically removed.