Product Data Sheet Show all documents

SikaProof®-808

Fully bonded FPO sheet membrane for below ground waterproofing

SikaProof®-808 is a fully-bonded FPO sheet membrane for external below-ground waterproofing of reinforced concrete structures. The membrane can be pre-applied. A special hybrid bonding layer on the membrane forms a permanent dual bond with the concrete structure to prevent lateral water migration between membrane and concrete. Overlap joints are sealed using cold-applied tapes or by thermal jointing.

  • Can be used as a pre and post-applied system
  • A+ Technology: Dual bond (mechanical and chemical) with concrete structure
  • High flexibility and crack-bridging capabilities
  • No lateral water underflow between concrete structure and waterproofing system
  • Easy to install with fully adhered joints
  • Overlap joints are sealed using thermal jointing or cold-applied tapes
 
Contact our Waterproofing Experts
Product Data Sheet Show all documents

Usage

SikaProof®-808 is used for:
  • Damp-proofing, waterproofing and concrete protection
SikaProof®-808 is used on the following structures:
  • Precast reinforced concrete structures
  • Cast-in-place reinforced concrete structures
  • Existing reinforced concrete structures

Advantages

  • Can be used as a pre and post-applied system
  • A+ Technology: Dual bond (mechanical and chemical) with concrete structure
  • High flexibility and crack-bridging capabilities
  • No lateral water underflow between concrete structure and waterproofing system
  • Easy to install with fully adhered joints
  • Overlap joints are sealed using thermal jointing or cold-applied tapes
 

Packaging

Roll width

1.00 m or 2.00 m

Roll length

25 m

Refer to the current price list for available packaging variations.

Colour

Colour

Light grey

Product Details

Sustainability / Certifications / Approvals

SUSTAINABILITY

  • Specific Environmental Product Declaration (EPD) in accordance with EN 15804. EPD independently verified by BRE Global

  • Contributes towards satisfying Materials and Resources (MR) Credit: Building product disclosure and optimization — Environmental Product Declarations under LEED® v4

  • Contributes towards satisfying Materials and Resources (MR) Credit: Building Product Disclosure and Optimization — Material Ingredients under LEED® v4

CERTIFICATES AND TEST REPORTS

  • CE marking and declaration of performance based on EN 13967:2012 Flexible sheets for waterproofing — Plastic and rubber damp proof sheets including plastic and rubber basement tanking sheet — Definitions and characteristics

  • General testing ASTM, Admaterials Technologies, Test report No. T20-16252

  • Watertightness functional test PG FBB Part 1, WISSBAU, Test report No. 2021-083-1

  • Watertightness functional test PG FBB Part 1, WISSBAU, Test report No. 2020-378-1

 
Product Information

Composition

Membrane Layer

FPO

Bonding Layer

Cement modified polymer

(A+ Technology)

Shelf life

24 months from date of production

Storage conditions

The Product must be stored in original unopened and undamaged sealed packaging in dry conditions and temperatures between +5 °C and +30 °C. Store in a horizontal position. Do not stack pallets of the rolls on top of each other, or under pallets of any other materials during transport or storage. Always refer to the packaging.

Effective thickness

Total thickness

(1.00 +0.10 / -0.05) mm

Thickness waterproofing layer

0.8 mm

Mass per area

(1.00 +0.10 / -0.05) kg/m²

(EN 1849-2)
System information

System structure

The following products are part of the pre-applied system:

  • SikaProof®-808 sheet membrane

  • SikaProof® Tape A+ N for detailing and for internal jointing
Technical Information

Resistance to impact

Method A, Hard support

≥ 800 mm

Method B, Soft support

≥ 800 mm

Resistance to static puncture

≥ 500 N

(ASTM E0154)

Tensile strength

Longitudinal (MD)

≥ 400 N/50mm

Transversal (CMD)

≥ 400 N/50mm

Longitudinal (MD) Method A

≥10 MPa

Transversal (CMD) Method A

≥10 MPa

Resistance to tear

Longitudinal (MD)

≥ 300 N

Transversal (CMD)

≥ 300 N

Joint shear resistance

≥ 100 N/50 mm

(EN 12317-2)

Crack bridging ability

No cracks occurred after 100 cycles at 3.2mm width

(ASTM C1305)

Foldability at low temperature

No cracks at -29 °C

(ASTM D1970)

Reaction to fire

Class E

(EN 13501-1)

Exposure to bitumen

28 days, +70 °C

Pass

Method A (24 hours, 60 kPa)

Pass

Watertightness

Method B, 24 hours at 60 kPa

Pass

Durability of watertightness against ageing

Aged 12 weeks at +70 °C, tested 24 hours at 60 kPa

Pass

Durability of watertightness against chemicals

Calcium hydroxide, aged 28 days at +23 °C, tested 24 hours at 60 kPa

Pass

Service temperature

Maximum

+35 °C

Minimum

-10 °C

Adhesion in peel

≥ 60 N / 50 mm with 90° angle after 28 days

(ASTM D903)

Resistance to lateral water migration

Up to 7 bar (71 m)

Pass

Application

Application Information

Ambient air temperature

Maximum

+45 °C

Minimum

+5 °C

Substrate temperature

Maximum

+60 °C

Minimum

+5 °C
Application steps

SUBSTRATE PREPARATION

Preconditions

The substrate is sufficiently stable to avoid movement during the construction works.

The substrate surface must be smooth, uniform and clean.

  1. IMPORTANT The substrate may be damp or slightly wet but avoid ponding water. Apply a Geotextile ≥ 300 g/m2 to protect the Product from sharp aggregates on the blinding concrete surface.

APPLICATION

IMPORTANT

Application by trained personnel

The application of this Product must only be carried out by an applicator that is trained or approved by Sika. The applicator must also be experienced in this type of application.

IMPORTANT

Reduced Product performance due to application in unsuitable weather conditions

  1. Do not install the membrane during continuous or prolonged rain, snowfall or sandstorms. 

IMPORTANT

Risk of leaks due to insufficient sealing of penetrations and construction joints

  1. Use additional Sika joint sealing solutions for connections around penetrations and for construction joints.

IMPORTANT

Reduced system performance due to permanent UV exposure

  1. The membrane must not be exposed to direct sunlight for more than 60 days.
  2. Proper concrete installation – mix design and workmanship – is required to achieve optimum bond of the membrane system to the concrete.

Reference must be made to Method Statement SikaProof-808 