Sika MaxTack® Ultra
Sika MaxTack® Ultra is a 1-component, solvent-free high tack adhesive with high load capacity.
- Powerful initial tack
- Fixing without tapes, nails or screws
- Very good adhesion to many substrates
- High load capacity
- Good workability
- Shrinkage-free hardening
Usage
Sika MaxTack® Ultra is designed for the indoor and outdoor bonding of various objects in and around houses such as cable channels, acoustic tiles, door sills, mirrors, construction materials, roof and wall coverings and cover plates.Sika MaxTack® Ultra adheres well to concrete, mortar, clinker, fiber cement, natural stone (e.g. granite), glazed and unglazed ceramic, wood, metal (galvanized and stainless steel, aluminum) and various types of plastics.
Advantages
- Powerful initial tack
- Fixing without tapes, nails or screws
- Very good adhesion to many substrates
- High load capacity
- Good workability
- Shrinkage-free hardening
Packaging
290 ml cartridge, 12 cartridges per box
Colour
White
Product Details
APPROVALS / CERTIFICATES
- Émissions dans l’air intérieur A+
Composition
Silane terminated polymer
Shelf life
Sika MaxTack® Ultra has a shelf life of 9 months from the date of production, if it is stored in undamaged, original, sealed packaging, and if the storage conditions are met.
Storage conditions
Sika MaxTack® Ultra shall be stored in dry conditions, where it is protected from direct sunlight and at temperatures between +5 °C and +25 °C.
Density
~1.40 kg/L | (ISO 1183-1) |
Shore A Hardness
>28 days | ~45 |
Tensile Strength
~2.2 N/mm2 | (ISO 37) |
Tear Propagation Resistance
~7.0 N/mm | (ISO 34) |
Service Temperature
−40 °C to +80 °C
Application
Ambient Air Temperature
+5 °C to +40 °C, min. 3 °C above dew point temperature
Substrate Temperature
+5 °C to +40 °C
Curing Rate
~3 mm/24 h (23 °C / 50% r.h.) | (CQP 049-2) |
Skinning time
~20 min (23 °C / 50% r.h.) | (CQP 019-1) |
Consumption
Using a nozzle with a 5 mm diameter, bead yield is approx. 15 m in length per 290 ml cartridge (approx. 20 ml per linear meter).
APPLICATION INSTRUCTIONS
For the application of Sika MaxTack® Ultra all standard construction guidelines apply.
SUBSTRATE PREPARATION
The substrate must be clean, dry, sound and homogeneous, free from oils, grease, dust and loose or friable particles. Paint, cement laitance and other poorly adhering contaminants must be removed. Sika MaxTack® Ultra adheres without primers and/or activators.
However, for optimum adhesion and critical, high performance applications, such as on multi-story buildings, highly stressed joints, extreme weather exposure or water immersion, the following priming and/or pre-treatment procedures shall be followed:
Non-porous substrates
Aluminium, anodised aluminium, stainless steel, PVC, galvanised steel, powder coated metals or glazed tiles have to be cleaned and pre-treated using Sika® Aktivator-205, wiped on with a clean towel. Before sealing, allow a flash-off time of > 15 minutes (< 6 hours).
Other metals, such as copper, brass and titanium-zinc, also have to be cleaned and pre-treated using Sika® Aktivator-205,wiped on with a clean towel. After the necessary flash-off time, use a brush to apply Sika® Primer-3 N and allow a further flash-off time of > 30 minutes (< 8 hours) before sealing the joints.
Porous substrates
Concrete, aerated concrete and cement based renders, mortars and bricks shall be primed using Sika® Primer-3 N applied with a brush. Before sealing, allow a flash-off time of > 30 minutes (< 8 hours).
For more detailed advice and instructions please contact our Technical Service Department.
Note: Primers are adhesion promoters. They are neither a substitute for the correct cleaning of a surface, nor do they improve the strength of the surface significantly.
CLEANING OF EQUIPMENT
Clean all tools and application equipment immediately after use with Sika® Remover-208. Once cured, residual material can only be removed mechanically.